We painted a 4 ele stepp-IR with marine topside paint purchased from
Lowe's. It was green and probably
made by Pettit don't remember. Anyway a check with the manufacturer
confirmed no conductive content.
No effect on the antenna tuning was apparent (this was an older antenna).
Paint is holding up well.
73, Joe K1JC
On Sun, Jan 4, 2015 at 12:38 PM, Howard W6HDG <W6HDG@arrl.net> wrote:
Happy New Year.
I asked this question on the Steppir Yahoo Group but didn't get an
adequate answer. I'm probably being way too compulsive but I'll ask it
here since there are so many experienced members.
I'm going to be preemptively painting my new DB18 with the marine topside
paint recommended by several Steppir forum members. This sounds smart
since the San Diego sun can be brutal to fiberglass and plastics.
I was concerned because the light blue "Blue Ice" Pettit Easypoxy Topside
Paint color I purchased contains 35% titanium dioxide and 10% aluminum
dioxide. Both the Pettit and Interlux brands of marine top coat in any
of the light colors seem to have quite a bit of the Ti02. Even Medium grays
have Ti02 as well as carbon black. Browns have iron oxide. In fact the only
marine paint which doesn't have any metallic sounding ingredient is Pettit
3350 Easypoxy Kelly Green Topside Paint. Could that be why Steppir chose
the green color for their fiberglass??
So here is where I am at. I wonder if my 4 tests with "Blue Ice" marine
paint were adequate to insure minimal interaction from the paint? Your
ideas welcomed.....
Test 1) I painted 6 inches of an 8 inch piece of 1" white PVC, allowed it
to dry for a day and placed it in the microwave along with a small cup of
water. I waited until the water boiled. The coated PVC remained cool and
was the same temp as the uncoated area.
Test 2) I coated a 30 inch piece of 1" PVC and allowed it to dry. I used
a dual band VHF/UHF magnetic whip on my car and measured the signal
strength of various distant repeaters. I then placed a plain piece of 30"
PVC over the entire whip and repeated the tests. Signal strengths were all
pretty much the same with a couple of weak repeaters showing up to one S
unit less than the bare tests. I then tested with the coated PVC. There
was no difference in any signal levels between the uncoated and coated PVC.
Test 3) I put two copper probes into water and measured resistance. It
measured between .3 and .5 megaohm. I then put the two copper probes
directly into the liquid paint and got zero resistance on all meter scales.
Test 4) I glued three strips of copper on an 8 inch piece of 1" white
PVC. The strips had a separation of 1/4 inch. Each strip had a wire lead
soldered to it. I then painted over the entire tube and let it dry for a
day. I could get no DC resistance measured between probes. I then placed
117VAC across the two outer probes. I tried to measure any leakage to the
center probe and was not able to measure any voltage.
So pretty compulsive, huh? Have I proven anything here or just created a
false sense of security? I figure that paint is much less reactive than
water. We know you can get electrocuted in a bathtub and that rainy
weather changes our SWR. I figure that marine paint, even if it has
metallic sounding compounds in it (short of metallic flakes like some auto
paints!) is OK for the Steppir.
73, Howard W6HDG _______________________________________________
_______________________________________________
TowerTalk mailing list
TowerTalk@contesting.com
http://lists.contesting.com/mailman/listinfo/towertalk
_______________________________________________
_______________________________________________
TowerTalk mailing list
TowerTalk@contesting.com
http://lists.contesting.com/mailman/listinfo/towertalk